Buckley D.;Oboroceanu D.;Quill N.;Lenihan C.;Ní Eidhin D.;Lynch R.
MRS Advances
Electrolyte Stability in Vanadium Flow Batteries
2018
January
Published
1
()
Optional Fields
energy storage environment kinetics modeling
3201
3212
Copyright © Materials Research Society 2018. The stability of VFB catholytes was investigated using both light-scattering measurements and visual observation. V2O5 precipitates after an induction time ¿ which shows an Arrhenius variation with temperature. The value of ¿ increases with increasing [S] and with decreasing [VV] but the activation energy remains constant with a value of (1.791±0.020) eV. Plots of ln ¿ against [S] and [VV] show good linearity and the slopes give values of ßS = 2.073 M-1 and ßV5 = -3.434 M-1 for the fractional rates of variation of ¿ with [S] and [VV], respectively. Combining the Arrhenius Equation with the observed log-linear variation of ¿ with [S] and [VV] provides a model for simulating the stability of catholytes. The addition of H3PO4 has a strong stabilizing effect on catholytes at higher temperatures. For example, at 50°C the induction time for precipitation for a typical catholyte is enhanced ~ 12.5-fold by 0.1 M added H3PO4. At concentrations of H3PO4 less than ~0.04 M, the precipitation time increases with increasing concentration at all temperatures investigated (30-70°C). At higher concentrations, induction time begins to decrease with increasing concentration of H3PO4: the changeover concentration depends on the temperature. Experiments at 70°C using other phosphate additives (sodium triphosphate, Na5P3O10, and sodium hexametaphosphate, (NaPO3)6) showed similar results to H3PO4.
10.1557/adv.2018.496
Grant Details